XOANONS?Additive
JIAZHI? Easy-cleaning functional resin
Model number
JIAZHI®JZ-9522
Specification
|
Composition |
Silicone modified hydroxyl acrylic resin solution |
|
Appearance |
Slight yellowish to yellow clear liquid |
|
Solvent |
BAC/PMA |
|
Content |
50±3%(140℃ 2h) |
|
Density |
1.00 -1.04g/ml(25±1)℃ |
|
Viscosity |
1000 -6000mPa·s |
|
Hydroxyl value |
152±5 mg KOH/g |
Note: This datasheet is intended to give typical results, not standard. Subject to COA.
Application system
Solvent-based system
Properties
● Increase slip. Improve hydrophobicity and oleophobicity.
● Provide anti-marker wiping performance.
● Provide lotus effect.
● Compared with anti-graffiti additive, better anti-graffiti effect and solvent-resistant wiping performance.
● Water contact angle＞100°
● Excellent anti-graffiti effect in light paint.
● Low temperature curing also has good anti-graffiti effect.
Storage stability
Store in a cool, dry place in the unopened original packaging for 36 months. Products that exceed the storage period can continue to be used after passing the inspection. It must be closed immediately after use.
Recommended formula
1. Suggestion for PU varnish formulation
|
|
Material |
Dosage% |
|||
|
Part A |
JZ-9522 |
76 |
|||
|
|
PMA |
22.65-22.74 |
|||
|
|
Dryer(1%) |
1 |
|||
|
|
WE-D8920BR(leveling agent) |
0.25 |
|||
|
|
WE-D980(defoamer) |
0.01-0.1 |
|||
|
|
Total |
100 |
|||
|
Part B |
N3390 |
23 |
1. Suggestions for the use of defoamers
Adding 0.01% XOANONS®WE-D980 to PU varnish does not affect the transparency of the paint solution; The color paint system can increase the amount of XOANONS®WE-D980 added by 0.1%.
2.NCO% of N3390=19.6, produced by Covestro, Germany.
3. After mixing A and B components, the storage period is 5-7 hours under the condition of a lid. Therefore, mixed materials should be used as soon as possible, otherwise it will be gelatinized and cannot be used.
4. Recommended baking temperature: 80 ° C for 1 hour or 150 ° C for 5 minutes, which could have better easy cleaning effect.
2. Suggestion for baking system formulation
|
Material |
Dosage |
||||
|
JZ-9522 |
50 |
||||
|
Butylated amino resin |
10 |
||||
|
Solvent |
38.5 |
||||
|
Adhesion promoter |
1 |
||||
|
Acid catalyst |
0.5 |
||||
|
Total |
100 |
||||
1.The amino resin used in this formulation is SANMU 582, which can be further adjusted according to specific requirements.
2. Recommended baking temperature: 150 ° C for 30 minutes or 210 ° C for 90 seconds.